The Effect Of Aluminium Trihydroxide (ATH) On The Thermal Properties Of Medium Density Fiberboard Made From EFB fiber , kenaf fiber and Hybrid EFB/Kenaf Fiber And Polyurethane As Binder

Paper details:
start with 1 page for first stage which is effect of Aluminium trihydroxide on thermal properties of medium density fiberboard made from by EFB fiber and Polyurethane as binder

So I need from the Top writer to make excellent discussion about how the ATH effect on the Thermal properties which is TGA

Also need him to refer to the figures in his discussion and also find related references to support the discussion.

No need to write any introduction or general topic about it, Just the discussion about the results in the table and figures.

Thank you
4.4.3 Thermogravemertic Analysis (TGA)

In the table below, thermogravimetric analysis (TGA) of medium density fireboard treated with fire retardants (Aluminum trihydroxide) was studied. The result indicates that fire retardants changed the reaction of thermal decomposition of the reactants (medium density fireboard). More specifically, the Aluminum trihydroxide (retardants) chemicals changed the pyrolysis of particle boards. This process resulted not only in increasing the number of char residuals, but also reduced the amount of volatile and the combustible vapors during the reaction.

Table 4.4 TGA results for the control KF-MDF and ATH-filled KF-MDF with 5, 10 and
15wt% of ATH
Content% T1 °C
Weight
Loss% T2 °C
Weight
Loss% T3 °C
Weight
Loss% Total Weight
Loss%
0 189 8 280 21 329 50 79

5 197 6 282 19 338 49 71

10 202 7 289 18 329 40 64

15 203 4 294 18 359 38 60

Figure 5.6 TGA results for the control KF-MDF and ATH-filled KF-MDF with 5, 10 and 15wt% of ATH

The Effect Of Aluminium Trihydroxide (ATH) On The Thermal Properties Of Medium Density Fiberboard Made From EFB fiber , kenaf fiber and Hybrid EFB/Kenaf Fiber And Polyurethane As Binder

Paper details:
start with 1 page for first stage which is effect of Aluminium trihydroxide on thermal properties of medium density fiberboard made from by EFB fiber and Polyurethane as binder

So I need from the Top writer to make excellent discussion about how the ATH effect on the Thermal properties which is TGA

Also need him to refer to the figures in his discussion and also find related references to support the discussion.

No need to write any introduction or general topic about it, Just the discussion about the results in the table and figures.

Thank you
4.4.3 Thermogravemertic Analysis (TGA)

In the table below, thermogravimetric analysis (TGA) of medium density fireboard treated with fire retardants (Aluminum trihydroxide) was studied. The result indicates that fire retardants changed the reaction of thermal decomposition of the reactants (medium density fireboard). More specifically, the Aluminum trihydroxide (retardants) chemicals changed the pyrolysis of particle boards. This process resulted not only in increasing the number of char residuals, but also reduced the amount of volatile and the combustible vapors during the reaction.

Table 4.4 TGA results for the control KF-MDF and ATH-filled KF-MDF with 5, 10 and
15wt% of ATH
Content% T1 °C
Weight
Loss% T2 °C
Weight
Loss% T3 °C
Weight
Loss% Total Weight
Loss%
0 189 8 280 21 329 50 79

5 197 6 282 19 338 49 71

10 202 7 289 18 329 40 64

15 203 4 294 18 359 38 60

Figure 5.6 TGA results for the control KF-MDF and ATH-filled KF-MDF with 5, 10 and 15wt% of ATH

The Effect Of Aluminium Trihydroxide (ATH) On The Thermal Properties Of Medium Density Fiberboard Made From EFB fiber , kenaf fiber and Hybrid EFB/Kenaf Fiber And Polyurethane As Binder

Paper details:
start with 1 page for first stage which is effect of Aluminium trihydroxide on thermal properties of medium density fiberboard made from by EFB fiber and Polyurethane as binder

So I need from the Top writer to make excellent discussion about how the ATH effect on the Thermal properties which is TGA

Also need him to refer to the figures in his discussion and also find related references to support the discussion.

No need to write any introduction or general topic about it, Just the discussion about the results in the table and figures.

Thank you
4.4.3 Thermogravemertic Analysis (TGA)

In the table below, thermogravimetric analysis (TGA) of medium density fireboard treated with fire retardants (Aluminum trihydroxide) was studied. The result indicates that fire retardants changed the reaction of thermal decomposition of the reactants (medium density fireboard). More specifically, the Aluminum trihydroxide (retardants) chemicals changed the pyrolysis of particle boards. This process resulted not only in increasing the number of char residuals, but also reduced the amount of volatile and the combustible vapors during the reaction.

Table 4.4 TGA results for the control KF-MDF and ATH-filled KF-MDF with 5, 10 and
15wt% of ATH
Content% T1 °C
Weight
Loss% T2 °C
Weight
Loss% T3 °C
Weight
Loss% Total Weight
Loss%
0 189 8 280 21 329 50 79

5 197 6 282 19 338 49 71

10 202 7 289 18 329 40 64

15 203 4 294 18 359 38 60

Figure 5.6 TGA results for the control KF-MDF and ATH-filled KF-MDF with 5, 10 and 15wt% of ATH